We have a technical team composed of several experienced technicians with rich practical experience and accumulation in the field of ceramic color pigments, Ceramic Inclusion Colour Red, Ceramic Roller Printing Colors Silver Gray, which ensures the product quality and production process. We strive for perfection, fully grasp the various needs of different users, and provide advanced, reliable, comprehensive and optimal technology and services. We have always pursued the enterprise spirit of excellence, continuous innovation, and the quality policy of persisting in quality and manufacturing products with value. Warmly welcome to cooperate and develop with us!

 

 FULLN CHEMICAL Ceramic Glaze Pigment Vanadium Blue FU-5701 (Turquoise blue sky blue) is a kind of inorganic blue pigment made of vanadium pentoxide, silica, zirconia, mineralizer and other raw materials. It is synthesized after calcination at high temperature. During the reaction, Zirconia (Zr4+), Silica (Si4+) and Vanadium (V4+) diffuse uniformly, then become the zirconite crystal structure. FULLN GLAZE ceramic glaze pigment Vanadium Blue is suitable for oxidizing and reducing atmosphere firing. FULLN Ceramic Glaze Pigment Vanadium Blue pigment is suitable for all kinds of glazes. Glaze with too much calcium is not conducive to good performance of the color.

 

CODE NO.	COLOR NAME	COLOR	COMPONENTS	Firing Temperature	CAS CODE
CERAMIC GLAZE COLORS
FU-5701	Turquoise Blue		Zr-Si-V	1050-1250℃	68186-95-8

The fineness of FULLN Ceramic Glaze Pigment Vanadium Blue pigment is less than 400 mesh, moisture is less than 0.5%. It can be used in ceramic floor tiles, ceramic wall tiles, art porcelains, sanitary wares, etc.

 

APPLICATIONS

Ceramics

Pottery

Sanitary ware

Tableware

Artware

Bricks

Porcelain

 

 

 

 

Preparation of Vanadium zirconium blue (Turquoise Blue sky blue)

1. Zirconium silicate powders can be completely decomposed and converted into alkali metals by using mixed base (lmol Na0H:1molKOH) at 800~850℃.

2. The hydrohalic acid treatment of zircon sand decomposition products is very simple and reasonable, and the treatment material can be directly used for pigment synthesis. This treatment material has high activity, which reduces the synthesis temperature of zircon.

3. The synthesis of vanadium-zirconium blue material is very sensitive to atmosphere and can only be formed in neutral or weak reducing atmosphere.

4. Two different cationic halides were used as compound mineralizers to strongly promote pigment dyeing and reduce the amount of vanadium compounds.

5. For the synthesized V-ZRSI0, the color can be stable within 1300℃, and the color intensity decreases after 1300℃.

6. When the glaze is adjusted, the amount of vanadium and zirconium added is 8%, the glaze with the same tone and color can be obtained.

 

 

 

We are committed to providing users with high-quality products and the best solutions, determined to be your best partner, and hope to make positive contributions to the development of the Pottery Oven Ceramic Fiber Module for Export industry. We will be glad to establish friendly business relationships with you! We know that good quality and the best service are the only way for us to achieve our customers and to achieve ourselves too.