Our firm since its inception, normally regards item top quality as company life, constantly make improvements to generation technology, improve product excellent and repeatedly strengthen organization total good quality management, in strict accordance with the national standard ISO 9001:2000 for Ceramic Roller Printing pigment, glass window color, Glass Pigments Red Brown. The company takes 'Quality is the life of an enterprise' and 'Customer satisfaction is our honor' as the eternal goal. We believe you will benefit from our professionalism soon. All our products are exported to clients in many countries. We'll continue to devote ourselves to market & product development and build a well-knit service to our customer to create a more prosperous future.

 

 FULLN CHEMICAL Ceramic Glaze Pigment Vanadium Blue FU-5701 (Turquoise blue sky blue) is a kind of inorganic blue pigment made of vanadium pentoxide, silica, zirconia, mineralizer and other raw materials. It is synthesized after calcination at high temperature. During the reaction, Zirconia (Zr4+), Silica (Si4+) and Vanadium (V4+) diffuse uniformly, then become the zirconite crystal structure. FULLN GLAZE ceramic glaze pigment Vanadium Blue is suitable for oxidizing and reducing atmosphere firing. FULLN Ceramic Glaze Pigment Vanadium Blue pigment is suitable for all kinds of glazes. Glaze with too much calcium is not conducive to good performance of the color.

 

CODE NO.	COLOR NAME	COLOR	COMPONENTS	Firing Temperature	CAS CODE
CERAMIC GLAZE COLORS
FU-5701	Turquoise Blue		Zr-Si-V	1050-1250℃	68186-95-8

The fineness of FULLN Ceramic Glaze Pigment Vanadium Blue pigment is less than 400 mesh, moisture is less than 0.5%. It can be used in ceramic floor tiles, ceramic wall tiles, art porcelains, sanitary wares, etc.

 

APPLICATIONS

Ceramics

Pottery

Sanitary ware

Tableware

Artware

Bricks

Porcelain

 

 

 

 

Preparation of Vanadium zirconium blue (Turquoise Blue sky blue)

1. Zirconium silicate powders can be completely decomposed and converted into alkali metals by using mixed base (lmol Na0H:1molKOH) at 800~850℃.

2. The hydrohalic acid treatment of zircon sand decomposition products is very simple and reasonable, and the treatment material can be directly used for pigment synthesis. This treatment material has high activity, which reduces the synthesis temperature of zircon.

3. The synthesis of vanadium-zirconium blue material is very sensitive to atmosphere and can only be formed in neutral or weak reducing atmosphere.

4. Two different cationic halides were used as compound mineralizers to strongly promote pigment dyeing and reduce the amount of vanadium compounds.

5. For the synthesized V-ZRSI0, the color can be stable within 1300℃, and the color intensity decreases after 1300℃.

6. When the glaze is adjusted, the amount of vanadium and zirconium added is 8%, the glaze with the same tone and color can be obtained.

 

 

 

Our exquisite management and details highlight the durability, reliability, safety of our products and our professionalism and confidence in the production of Red Iron Oxide Inorganic Pigment for Concrete Brick. We are committed to providing a professional, intelligent and efficient service model, so that high-quality, leading products can better meet customers' needs. We have long-term emphasis on research and development work, and continue to provide innovative products that meet customer requirements.

Hot Tags: ceramic glaze pigment vanadium blue, China, manufacturers, suppliers, factory, custom, wholesale, bulk, in stock, Ceramic Roller Printing Pigments V Yellow, Enamel Colors Coffee Brown, Ceramic Inclusion Colors, Ceramic Dry Mixed mixing Colors Black, green stained glass, Ceramic Ink Pigments colors